不同时间对钛表面微弧氧化处理后与瓷结合强度的影响
|
|
【制药类毕业论文】 作者:李健学,张玉梅,憨勇,刘啸晨,于凡【关键词】 微弧氧化;时间;结合强度;肽Effects of microarc oxidation time on bonding strength of titanium to porcelain 【Abstract】 AIM:To study the effects of time length of microarc oxidation (MAO) on the titaniumceramic bonding strength. METHODS: Titanium samples were treated with MAO in a Na2SiO3 electrolytic solution with duty cycle 0.04, frequency 500 Hz, and voltage 300 V. According to the different oxidation time, experimental groups consisted of 3, 6, 10 min groups. The nonMAO samples were used as a control group. The surface of the samples was observed by scanning electron microscope (SEM). The samples were bonded to porcelain. The bonding strength of the samples was measured by a threepoint bending test. RESULTS: The bonding strength (MPa) of the samples to porcelain in 3, 6, 10 min groups and control group was 56.4±0.8, 40.4±2.3,36.0±3.0,32.2±1.9. T
|
|
|