Preparation and quality evaluation of oleanolic acidloaded solid lipid nanoparticles
【Abstract】 AIM: To prepare the oleanolic acidloaded solid lipid nanoparticles (OASLN), determine the content of oleanolic acid in OASLN, and evaluate its quality. METHODS: OASLN were prepared by filmultrasound dispersion technique. The encapsulation efficiency and appearance of solid lipid nanoparticles were studied. RESULTS： The appearance of prepared solid lipid nanoparticles was regular with the diameter being （62.0±10.3） nm, the encapsulation efficiency was 98.29% and the loading rate was 8.17%. CONCLUSION： The selected preparation technique of OASLN is rational and practicable. It provides experimental evidence for developing a new oleanolic acid injection.
【Keywords】 oleanolic acid； solid lipid nanoparticles； quality evaluation
【摘要】 目的西医学 免费论文下载：对齐墩果酸固体脂质纳米粒的西医学 免费论文下载制备工艺和含量测定方法进行研究，并对其质量进行评价. 方法：采用薄膜超声分散法制备齐墩果酸固体脂质纳米粒，并对其包封率、形态等性质进行研究. 结果：制得齐墩果酸固体脂质纳米粒形态均匀圆整、粒径范围为(62.0±10.3) nm，包封率为98.29%，载药量为8.17%. 结论: 选择薄膜超声分散法制备齐墩果酸固体脂质纳米粒方法可行,为开发齐墩果酸新型注射制剂提供了实验依据.
【关键词】 齐墩果酸；固体脂质纳米粒；质量评价
0引言
齐墩果酸（oleanolic acid, OA）是一种五环三萜类化合物，国内临床上主要用于慢性肝炎的治疗以及多方面保肝作用［1］. 固体脂质纳米粒(solid lipid noparticles，SLN)系指以固态的天然或合成类脂如大豆磷脂、三酰甘油等为载体材料，将药物包裹或内嵌于类脂核中，制成粒径约为10～1000 nm的固体胶粒给药系统［2］. 本实验我们以大豆磷脂为载体，采用薄膜超声分散法制备齐墩果酸固体脂质纳米粒, 期望提高齐墩果酸的肝脏靶向性.
1材料和方法
1.1材料LC10AVP高效液相色谱仪（日本岛津公司），SephadexG50凝胶（Sigma公司），RE52旋转蒸发仪（上海亚荣生化仪器厂），KQ250型超声波发生器（江苏昆山淀山湖检测仪器厂），BP190S电子天平（德国赛多利斯），齐墩果酸（陕西慧科公司,批号050322），大豆磷脂（上海太伟药业有限公司，批号040716）,其他试剂均为国产分析纯.
1.2方法
1.2.1齐墩果酸固体脂质纳米粒的制备精密称取处方量物质于100 mL圆底烧瓶中，加入15 mL氯仿溶解. 39℃旋转蒸发10 min除去氯仿，在烧瓶壁上形成一层薄膜. 加入60 mL/L甘露醇水溶液15 mL，40℃水浴超声30 min,0.45 μm微孔滤膜过滤，分装于安瓿中［3］.
|
| | |