Nano-sized TiO2 Film Preparation and Photocatalytic
Degradation of TrichloromethaneLIU Zhao-hui1，QU Ling-po2，SHI
Dong-wen3

(1.Department of Chemical Industry,Zhengzhou
Institute of Light Industry,Zhengzhou 450002,China; 2.Department of
Chemistry,Zhengzhou University,Zhengzhou 450052,China; 3.Zhengzhou
City General Water Supply Co.,Zhengzhou 450052,China)

　　Abstract：The nano-sized TiO2 film is prepared by sol-gel
method and the crystal is of anatase type.Addition of Polyethylene
Glycol 2000 (PEG 2000) will make the film in the porous shape,which
will affect transmittancy of the film.The nano-sized film has
favorable catalytic effect on the photocatalytil degradation of
CHCl3,and the porous nano-sized film has much more catalytic
effect.The decomposition r
ate of CHCl3 under the photocatalytic
condition is approximated to 90%.
　　Keywords:nano-sized
TiO2 film;photocatalysis;trichloromethane (CHCl₃)

　　纳米TiO2可将许多有机化合物氧化、分解成CO₂和H₂O，在处理有机污染物方面有极好的应用前景［1～3］，但粉末状纳米TiO₂悬浮于光催化体系中存在流失、回收及分离等诸多问题［3］。近年来，国内外就纳米TiO₂光催化剂的固定和纳米TiO₂薄膜的制备做了许多工作，其中溶胶法制备纳米TiO₂薄膜是目前研究最多的一种制备方法^［4］。相对于化学气相沉积和溅射制膜而言，该法具有设备简单、容易控制、条件温和、能大面积制膜等优点。试验采用溶胶法在普通载玻片上以1.5
mm/min的浸提速度制备光催化薄膜，分别以SEM、XRD、UV对纳米TiO₂薄膜进行表征，并进行了纳米TiO₂薄膜光催化分解CHCl₃的研究。

1　试验内容及方法

1.1　纳米TiO₂薄膜的制备
　　溶胶制备方法见参考文献［5］，得到稳定、均匀、清澈透明的淡黄色溶胶后，以洁净载玻片作基体，浸入溶胶中以浸渍提拉法制备，提拉速度为1.5
mm/min。湿膜在100 ℃时干燥5
min后，放入马福炉内以500 ℃焙烧1
h，重复上述操作可得不同厚度的薄膜。
1.2　纳米TiO₂薄膜的表征
　　用H—600(Hittachi)电镜观察纳米TiO2薄膜的表面状态和薄膜厚度；以D/MAX—3B
XRD、Cu靶、35 V—30
mA来确定纳米TiO₂薄膜的晶型和粒径；以UV—1601PC紫外可见分光光度计测量纳米TiO₂薄膜在200～800
nm范围内的透光率。
1.3　光催化试验
　　在自制玻璃反应器中放入一定浓度的CHCl₃水溶液和面积为5cm₂的纳米TiO₂薄膜，以8