| | | 四元共聚物的合成及缓蚀阻垢性能研究
| | 给水工程论文
摘要：以水为溶剂，采用过氧化物一次磷酸盐为引发体系，用马来酸本刊酐(ma)，2-丙烯酞胺-2-甲基丙碳酸(amps)，丙烯酸(aa)为单体在水相中合成了ma－amps－aa－poca共聚物。试验表明该共聚物适于ph小于9的给水工程论文水质。在文中所述试验条件下，当共聚物的给水工程论文用量分别达到35mg/l和50mg/l，缓蚀率和阻垢率均达到95％。
关键词：共聚物 缓蚀剂 阻垢剂
中图分类号：tu991.27
文献标识码：a
文章编号：1009－2455(2002)03－0010－03
study on the polymerization and
corrosion and scale inhibition behaviours of a
tetra-copolymer
sun zhe,zeng xin-ping,li yi-jiu,
ni ya-ming
(chemistry department of tongji
university, shanghai 200092, china)
abstract: a copolymer called ma-amps-aa-poca
was prepared from ma(maleic anhydride),
apms(2-acrylamido-2-methylpropane sulfonic acid),and
aa(acrylic acid )in water phase by using
peroxide-hypophosphite as initiator. the tests with the
copolymer as inhibitor show that the average corrosion
and scale inhibition efficiency achieves 95% when
copolymer dose in 30mg/l and 50 mg/l respectively at
ph＜9 and other conditions mentioned in this
paper.
key words:copolymer;polymerization;
corrosion inhibitor; scale inhibitor
磺酸共聚物因对磷酸钙垢有良好抑制作用，能有效分散金属氧化物且能稳定锌和有机磷酸等优点[1]，得到了迅速发展。而膦酸基团又具有很好的缓蚀性能。本文以马来酸酐(ma)，2-丙烯酸胺-2-甲基丙碳酸(amps)，丙烯酸(aa)等为单体合成了一种新型四元缓蚀阻垢共聚物(ma－amps－aa－poca)，并探讨了该共聚物的缓蚀阻垢性能，考察了水质条件变化以及水中常见离子对其性能的影响。
1 实验部分
1.1
主要原科
马来酸酐(ma)、丙烯酸(aa)、次磷酸二氢钠(nah2po2·2h2o)为化学纯；amps为工业品；cacl2、feso4·7h2o、nahco3、edta等均为分析纯。
1.2
ma-amps-aa-poca的合成
在装有冷凝器、温度计、滴液漏斗和电子恒温恒速搅拌器的四颈烧瓶中加入一定量的马来酸酐、引发剂，再加入丙烯酸、amps等控温反应2－4h，然后再保温2－3h，得到浅黄色透明共聚物。
1.3
静态阻垢性能测定
1.3.1
静态阻碳酸钙垢实验
试验温度为80℃，浓缩倍数1.5，试验水质为：ph为9，ca2+(以caco3计)250mg/l，hco3-(以ca-co3计)250mg/l，恒温10h。
1.3.2
静态阻磷酸钙实验
试验温度为80℃，试验水质为：ph为9，ca2+(以caco3计)250mg/l，po43-5mg/l，不浓缩，恒温10h。
1.4
旋转挂片腐蚀实验
试验温度为50±1℃，转速75r/min脓缩倍数1.5倍，水质条件为cl-100m/l，hco3-100mg/l，so42-100mg/l。试片材质为20＃碳钢(gb699－65)。
2 共聚物性能的综合评价
2.1 共聚物用量
共聚物用量对缓蚀阻垢效果影响见图1，图2。
|
| | |
| | | | <<<<<全文未完>>>>> 全文字数约1858字 | |
| | |
| |
|
教育论文中心