摘要：本文提出了一种改进的网桁索膜表面吸水率试验用于评估混凝土的网桁索膜养护效果，养护的充分与否通过混凝土试件不同深度处的孔结构的差异来判定。研究中利用高性能混凝土的自养护来对此方法的可行性进行了试验验证。试验结果表明：利用此方法测试的孔结构参数受养护条件的显著影响；养护措施不好的情况下，不同深度处混凝土试件的吸水率与孔结构参数差异显著；本方法操作简单、快捷，可以用来评价混凝土的养护效果，尤其适用于高性能混凝土。
关键词：表面吸水率 孔结构 养护 高性能混凝土
A New Procedure for Evaluating the Adequacy of Curing for High
Performance Concrete
ZHAN Bing-gen DING Yi-bing
（School
of Civil Engineering, Hefei University of Technology, Hefei 230009, China）
Abstract：An improved absorption test for assessment
of the adequacy of curing for concrete is present. In this approach, the curing
efficiency is evaluated by determining the differences in pore structure at
difference depths in test specimens. The approach was applied for self-curing
of high performance to verify its feasibility. Experimental results show that
the pore structure determined by this approach was sensitive to the curing
conditions. There is a significant difference in absorptivity and pore
structure at varied depth in concrete in poor curing procedure. The approach,
operated simply and quickly, can be used to determine the adequacy of curing
for concrete, especially for high performance concrete.
Key words: absorptivity;
pore structure; curing; high performance concrete
0
引言
养护是混凝土工程中重要的环节，对性能影响很大。对于高性能混凝土（HPC）也是如此，而且由于HPC本身的特点，如掺有活性掺料、水胶比低等特点，良好的养护就更为必要。然而目前混凝土结构现场养护往往被忽视，对于HPC还没有切实有效的养护措施，也缺乏有效的方法用于评估现场高性能混凝土养护的有效性[1]。本研究目的就是试图在混凝土表面吸水率实验的基础上，提出一种混凝土养护效果的评估方法，并用高性能混凝土自养护方法来验证试验的可行性。[1]
表面吸水率试验首先被Powers和Brownyard用于研究硬化水泥浆体[2]，Dolch应用此方法研究石灰石骨料的孔结构[3]。Ephraim Senbetta首次利用吸水率指标来评价普通混凝土的养护效果[4]。ASTM C 1511也利用表面吸水率指标来评价混凝土养护的有效性，认为普通混凝土Kα≤3.7×10-6cm2/s，意味着养护效果良好。但是高性能混凝土的组织结构已经不同于普通混凝土，因此仅仅利用表面吸水率指标来评价高性能混凝土的养护效果已经不够全面，对于高性能混凝土必须有能够全面预估耐久性能指标的评价标准。由于混凝土性能与孔结构密切相关[5、6]，因此从微观结构出发，更有利于估测其养护效果以及长期性能。
|